SCC behaviour of laser powder bed fused 316L stainless steel in high-temperature water at 288 °C
Julkaisuvuosi
2023
Tekijät
Que, Zaiqing; Riipinen, Tuomas; Goel, Sneha; Revuelta, Alejandro; Saario, Timo; Sipilä, Konsta; Toivonen, Aki
Tiivistelmä
Stress corrosion cracking (SCC) behaviour of laser powder bed fused stainless steel 316L was evaluated with U-bend testing in oxygenated high-temperature water at 288 °C. The effects of solution annealing temperature (1066, 1150 and 1200 °C), surface finish (as-built and wire cut) and the sample orientations on the SCC behaviour were studied. The results show that a higher annealing temperature introduces further recrystallization, coarsening of the oxide inclusions and a decrease in resistance to SCC. A wire cut surface leads to a higher susceptibility to SCC than the as-built surface. Sample orientation was found not to affect the SCC susceptibility.
Näytä enemmänOrganisaatiot ja tekijät
Teknologian tutkimuskeskus VTT Oy
Toivonen Aki
Sipilä Konsta
Goel Sneha
Saario Timo
Riipinen Tuomas
Que Zaiqing
Julkaisutyyppi
Julkaisumuoto
Artikkeli
Emojulkaisun tyyppi
Lehti
Artikkelin tyyppi
Alkuperäisartikkeli
Yleisö
TieteellinenVertaisarvioitu
VertaisarvioituOKM:n julkaisutyyppiluokitus
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessäJulkaisukanavan tiedot
Lehti
Volyymi
214
Artikkelinumero
111022
ISSN
Julkaisufoorumi
Julkaisufoorumitaso
3
Avoin saatavuus
Avoin saatavuus kustantajan palvelussa
Kyllä
Julkaisukanavan avoin saatavuus
Osittain avoin julkaisukanava
Kustantajan version lisenssi
CC BY
Rinnakkaistallennettu
Ei
Muut tiedot
Tieteenalat
Materiaalitekniikka
Avainsanat
[object Object],[object Object],[object Object],[object Object],[object Object],[object Object],[object Object]
Kieli
englanti
Kansainvälinen yhteisjulkaisu
Ei
Yhteisjulkaisu yrityksen kanssa
Ei
DOI
10.1016/j.corsci.2023.111022
Julkaisu kuuluu opetus- ja kulttuuriministeriön tiedonkeruuseen
Kyllä