Stress corrosion cracking initiation susceptibility of Alloy 182 with different surface treatments
Julkaisuvuosi
2022
Tekijät
Que, Zaiqing; Saario, Timo; Toivonen, Aki; Ehrnstén, Ulla
Tiivistelmä
The effects of machining surface preparations on the stress corrosion cracking (SCC) susceptibility in boiling water reactor environment were evaluated for Alloy 182 weld metal. Constant extension rate tensile test, constant load test and electrochemical tests (passivation, current-voltage curves and electrochemical impedance spectroscopy) showed that the surface treatments strongly influence the resistance to SCC initiation. The machining-induced deformation and surface oxide layer from the surface treatments affect the re-passivation behaviour and SCC initiation susceptibility. The SCC susceptibility of the studied surface treatments was found following the sequence of shot peened > industrial surface milled > polished > advanced manufactured surface.
Näytä enemmänOrganisaatiot ja tekijät
Julkaisutyyppi
Julkaisumuoto
Artikkeli
Emojulkaisun tyyppi
Lehti
Artikkelin tyyppi
Alkuperäisartikkeli
Yleisö
TieteellinenVertaisarvioitu
VertaisarvioituOKM:n julkaisutyyppiluokitus
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessäJulkaisukanavan tiedot
Lehti
Volyymi
196
Artikkelinumero
110037
ISSN
Julkaisufoorumi
Julkaisufoorumitaso
3
Avoin saatavuus
Avoin saatavuus kustantajan palvelussa
Kyllä
Julkaisukanavan avoin saatavuus
Osittain avoin julkaisukanava
Kustantajan version lisenssi
CC BY
Rinnakkaistallennettu
Ei
Muut tiedot
Tieteenalat
Kemia; Materiaalitekniikka
Avainsanat
[object Object],[object Object],[object Object],[object Object],[object Object]
Kieli
englanti
Kansainvälinen yhteisjulkaisu
Ei
Yhteisjulkaisu yrityksen kanssa
Ei
DOI
10.1016/j.corsci.2021.110037
Julkaisu kuuluu opetus- ja kulttuuriministeriön tiedonkeruuseen
Kyllä